1. Kuyambitsa chitsulo cha Q315NS asidi-resistant:
Mtundu: Q315NS
Dzina lazogulitsa: Chitsulo cha sulfuric acid chopanda kutentha kwa mame
Executive muyezo: GB/T28907-2012
Kukula, mawonekedwe, kulemera ndi kupatuka kovomerezeka kwa Q315NS kuyenera kutsatira GB/T709.

2. Tanthauzo la chitsulo cha Q315NS chosamva asidi:
Q315NS njira yofotokozera: Q-chilembo choyamba cha pinyin yaku China cha "qu" mu mphamvu zokolola;315 - malire otsika achitsulo, mu MPa;NS—chilembo choyamba cha pinyin yaku China cha “resistant” ndi “acid” motsatana.Q315NS asidi-resistant chitsulo amatanthauza kuwonjezera kuchuluka kwa zinthu alloying zitsulo kuonjezera kukana asidi sulfuric opangidwa ndi kuphatikiza sulfure trioxide ndi madzi pansi pa mame pamene chitsulo poyera mpweya sulfuric (monga chumuni chachitsulo chokhala ndi mpweya wotulutsa mpweya).Kuchita kwa dzimbiri.

3. Chemical zikuchokera Q315NS asidi-resistant chitsulo:
Zinthu za CSiMnPSCrCuSbQ345NS≤0.15≤0.55≤1.20≤0.035≤0.0350.30-1.200.20-0.50≤0.15

4. Zipangizo zamakina a Q315NS acid-resistant zitsulo: zokolola zakuthupi mphamvu Ra MPa kumakoka mphamvu Ra MPa elongation pambuyo fracture A%Q315NS≥315≥440≥22Q345NS≥345≥470≥20

5. Kukana kwa dzimbiri kwa Q315NS chitsulo chosagwira asidi:
Malinga ndi njira yoyesera yomwe yafotokozedwa mu JB/T7901, kuchuluka kwa dzimbiri sikupitilira 10mm/a (0.89mg/cm²*h, 30% kuyerekeza ndi kuchuluka kwa dzimbiri kwa Q235B pansi pa kutentha kwa 20℃, sulfuric). asidi ndende 20%, ndi kumizidwa kwathunthu kwa maola 24);Pansi pa kutentha kwa 70 ℃ ndi kumizidwa kwathunthu kwa 24h, kuchuluka kwa dzimbiri sikuposa 250mm/a (22.4mg/cm²*h, 50% poyerekeza ndi kuchuluka kwa dzimbiri kwa Q235B).